Hello everyone.
I have worked with this winder for few weeks now. I'm still unable to get DH Linear to work properly. The problem seems to be that the executor software doesn't recognize the position signal from the motor. If i check…
Read more…Hello everyone, Great to be part of this forum for this machine, already thinking about how I can redesign the squeeze without even winding yet.
I have been having extensive trouble and been trying to get my 4-axis X-winder up and…
Hey guys, we tested out a few new mods to our machine, and had some great success with our last wind.We removed the plate/roller/lucky band squeege system as it was proving inconsistant.We made a new bracket for the squeege roller, out of two 90…
Read more…Hello everyone,
I'm excited to finally have our machine up and running and winding mandrels, but would really love to hear guys experiences in the resin ratio / viscosity used, and how to control the layer…
Read more…Hi everyone!
I use XW-2 and have a problem that I hadn't managed to solve. The end winds slide down of mandrel when the carrige changes direction. How can I fix the plies?
My ideas as follows:
1. to change a winding angle at the…
Read more…The 4 axis machine currently looks pretty good at winding pressure vessels. But I would one day like to wind complex bicycle related parts like T joints and elbows. These seems to be able to be filament wound (videos below) and I was wondering if…
Read more…I just checked out the 3 axis winding demo and it looks like it would allow for a better part than the 2 axis, by providing better pressure distribution. How much difference would this make to the parameters (bending stiffness to weight ratio…
Read more…The upgrades to the new 2 and 4 axis models look great and I am looking to do the following upgrades and was wondering whether anyone had some feedback on these proposals or had thought of doing something similar?
Relocate spool holders…
Read more…I have been having some problems getting a grade A finish on my parts and was wondering if anyone is achieving this? My problem is that as the tape contracts it leaves some impurities, like resin rich areas which then have to be sanded back,…
Read more…So, after producing 15 or so poles on my x winder I was wondering what everyone has been using for their mandrels? So far it looks like cardboard is popular, but I imagine this would be too inconsistent for my parts. I have read that mandrels…
Read more…Hello everyone,
How have you been going with winding angle selection? I understand the 90’ is optimal for burst strength (which many of you will use for rocketry), but I am generally trying to optimise bending stiffness. I started…
Read more…I have been slowly been getting better at making poles: Here are some of my early frankenpoles:…